Ester Soluble Vinyl Chloride and Vinyl Acetate Copolymers
(Sinfeng)
| Name | Composition | K Value (Molecular Weight) | Equivalent to |
|---|---|---|---|
| MLC-14-55 | Vinyl Chloride: 86 ± 1% Vinyl Acetate: 14 ± 1% | 46–48(27000) | VYHH (DOW) |
| MLC-10-80 | Vinyl Chloride: 90 ± 1% Vinyl Acetate: 10 ± 1% | 58–60(約44000) | VYNS-3 (DOW) |
| LC-40 | Vinyl Chloride: 60 ± 2% Vinyl Acetate: 40 ± 2% | 48–50(約55000) | H40/50 (WACKER) |
Ester Soluble Vinyl Chloride and Vinyl Acetate Copolymers (Hanwha)
| Name | Composition | K Value (Molecular Weight) | Equivalent to |
|---|---|---|---|
| CP-430 | Vinyl Chloride: 85% Vinyl Acetate: 15% | 50(48200) | - |
| CP-450 | Vinyl Chloride: 87% Vinyl Acetate: 13% | 53(53300) | - |
| CP-710 | Vinyl Chloride: 90% Vinyl Acetate: 10% | 58(68000) | - |
Carboxyl-Modified Vinyl Chloride–Vinyl Acetate Terpolymer (Sinfeng)
| Name | Composition | K Value (Molecular Weight) | Carboxyl Content (%) | Equivalent to |
|---|---|---|---|---|
| VAMA | Vinyl Chloride: 86 ± 1% Vinyl Acetate: 13 ± 1% Maleic Acid: 1 ± 0.2% | 45–47 (approx. 27,000) | 1±0.2 ％ | - |
| VMA | Vinyl Chloride: 81 ± 1% Vinyl Acetate: 17 ± 1% Maleic Acid: 2 ± 0.2% | 32–36 (approx. 15,000) | 2±0.2 ％ | VMCA (DOW) |
Hydroxyl-Modified Vinyl Chloride–Vinyl Acetate Terpolymer (Sinfeng)
| Name | Composition | K Value (Molecular Weight) | Hydroxyl Content (%) | Equivalent to |
|---|---|---|---|---|
| MVAH | Vinyl Chloride: 90 ± 1% Vinyl Acetate: 3 ± 1% Vinyl Alcohol: 7 ± 0.5% | Approx. 46 (approx. 27,000) | 1.8–2.3 ％ | Solbin A (Nissin) |
| MVOH | Vinyl Chloride: 81 ± 1% Vinyl Acetate: 4 ± 1% Hydroxyalkyl Acrylate: 15 ± 1% | 39–41 (approx. 15,000) | 1.9–2.1 ％ | Solbin TA3 (Nissin) |
Special-Modified UV Exclusive Use Vinyl Resin Series (Sinfeng)
| Name | Composition | K Value (Molecular Weight) | Hydroxyl Content (%) | Equivalent to |
|---|---|---|---|---|
| PG-HC | Vinyl Chloride: 84 ± 1% Vinyl Acetate: 10 ± 1% Vinyl Alcohol: 6 ± 0.5% | 48–50 (approx. 30,000) | 1.8–2.3 ％ | VAGH (DOW) |
| TLC40/43 | Vinyl Chloride: 60 ± 2% Vinyl Acetate: 40 ± 2% | 40–44 (approx. 30,000) | - | H40/43 (WACKER) |